Product Details:
|
| Material: | High Chrome Carbon Steel, 100CrSiMn6-4,GCr15SiMn | Grade: | G60 Or G40 |
|---|---|---|---|
| Hardness: | HRc 60-67 | Application: | Wind Turbine Bearing, Slewing Ring Bearing |
| Surface: | Smooth Surface, Polished Finish | Properties: | Good Size Stability And Anti-abrasion |
| Free Samples: | Can Be Supplied | Package: | Plastic Bag + Cardboard Box + Wooden Pallet |
| Highlight: | 60.01mm Large Solid Steel Balls,60.04mm Large Solid Steel Balls,60.04mm Solid Metal Balls |
||
59.99mm(2.36181"), High Chrome Steel Balls For Big Bearing, G40 Or G60
Introduction
High-carbon chromium bearing steel refers to high-carbon alloy steel with a chromium content of 1.40-1.65%. Its characteristics are the microstructure after heat treatment is relatively uniform and stable, good wear resistance, high stress fatigue strength, good dimensional stability and wear resistance. have good hardenability, and extremely strict control of sulfur and phosphorus. It is a high-grade high-quality steel. Make cold work mold steel. Specific gravity: 7.81.
This type of steel can meet the processing requirements under general working conditions. The brand numbers of ordinary high-carbon chromium bearing steel are GCr15 and GCr15SiMn. The performance of these two types of bearings is basically the same. But the hardenability of GCr15SiMn is better than GCr15, so GCr15SiMn is used for relatively large bearing parts.
Because GCr15SiMn has high crack sensitivity and low impact resistance, it cannot fully meet the requirements for thick-walled bearings and mine bearings. Therefore, the railway department does not allow the use of CGr15SiMn on passenger car bearings. It is also limited to thick-wall rolling mills and mining machinery under large and compact loads.
The chromium ball is made of the highest quality chromium alloy steel and is quenched to achieve maximum strength and service life. Ideal applications for chrome balls include rolling media, spray tank mixing, ball bearings, wind turbine bearings and linear motion components. The most widely used in various industries.
The surface of our chrome steel balls is extremely precise and smooth, ensuring that you will not find any defects such as flatness, dents, soft spots and cuts.
We mainly produce chrome steel with sizes ranging from 7.9375mm to 82.55mm. The main material is high chromium GCR15 or GCR15SiMn. Our balls are mainly used in the wind energy industry.Our products enjoy high evaluation and satisfaction among customers.
Our services and advantages
1. High precision, high hardness, high speed.
2. Can be customized according to your needs.
3. Can provide small and non-standard balls.
4. Reasonable price.
5. Technology: low vibration, low noise, high precision and durability.
6. Our quality is higher at the same price, our price is lower at the same quality.
7. Our delivery time is shorter than other factories for the same qty of bearings.
8. We provide the best service. A good reputation has always been the advantage of our company.
Parameter
| Ball Diameter | Grade | Hardness | Material |
| 59.99mm(2.36181") | G40 or G60 | HRc 60-67 | GCr15SiMn,100CrSiMn6-4,SUJ3,52100 |
Product Details
| Product Name | High Quality Chrome Steel Balls |
| Size range | Ø 59.94 mm – Ø 60.06 mm(GCr15SiMn/SUJ3/100CrMn6 Chrome Steel Balls) |
| Quality grades | G40 or G60 for balls Ø59.94mm to 60.06mm |
| Hardness |
For 60mm group ball, a minumun core hardness at centre of the ball shall be HRc55. minumun hardness at surface of the ball shall be HRc60. minumun hardness at depth of 15% ball diameter shall be HRc58. |
| Application | The High Quality Chrome Steel Balls are mainly applied in slewing ring bearing for wind turbines,such as single/double row ball bearing,single cross roller bearing,three roller bearing, double row angular contact ball bearing. |
Grade and Tolerance
| Precision / Grade |
Ball Diameter Tolerance |
Deviation from Spherical Form |
Maximun surface roughness |
Lot diameter variation |
| G40 | 1 | 1 | 0.06 | 2 |
| G60 | 1.5 | 1.5 | 0.08 | 3 |
| Chemical Composition | ||||||
| C% | Si% | Mn% | Cr% | Cu% | C% | |
| 52100 | 0.98~1.10 | 0.15~0.35 | 0.25~0.45 | 1.30~1.60 | 0.98~1.10 | |
| GCr15 | 0.95~1.05 | 0.15~0.35 | 0.25~0.45 | 1.40~1.65 | 0.25 | 0.95~1.05 |
| GCr15SiMn | 0.95~1.05 | 0.45~0.75 | 0.95~1.25 | 1.40~1.65 | 0.25 | 0.95~1.05 |
| 100Cr6 | 0.93~1.05 | 0.15~0.35 | 0.25~0.45 | 1.35~1.60 | 0.93~1.05 | |
| SUJ2 | 0.95 or 1.10 | 0.15 or 0.35 | 0.50 max | 1.30~1.60 | 0.95 or 1.10 |
|